| 物理性能 |
值/单位 |
测试标准 |
测试条件 |
密度
|
1.04 g/cm³ |
ISO 1183 |
|
密度
|
1.04 g/cm³ |
ASTM D792 |
|
收缩率
|
|
|
|
纵向(Flow)
|
0.89 % |
ISO 294 |
flow, 24 hrs
|
纵向(Flow)
|
0.89 % |
ASTM D 955 |
flow, 24 hrs
|
横向(Across Flow)
|
1.15 % |
ASTM D 955 |
xflow, 24 hrs
|
横向(Across Flow)
|
1.15 % |
ISO 294 |
xflow, 24 hrs
|
吸湿率
|
0.07 % |
ISO 62 |
23°C / 50% RH
|
吸湿率
|
0.06 % |
ASTM D 570 |
50% RH, 24 hrs
|
| 机械性能 |
值/单位 |
测试标准 |
测试条件 |
拉伸强度
|
|
|
|
屈服(yld)
|
46 Mpa |
ASTM D638 |
|
屈服(yld)
|
38 Mpa |
ISO 527 |
|
断裂(brk)
|
41 Mpa |
ISO 527 |
|
断裂(brk)
|
42 Mpa |
ASTM D638 |
|
拉伸延伸率
|
|
|
|
屈服(yld)
|
4.2 % |
ASTM D638 |
|
屈服(yld)
|
3.2 % |
ISO 527 |
|
断裂(brk)
|
52.3 % |
ASTM D638 |
|
断裂(brk)
|
37.3 % |
ISO 527 |
|
弯曲强度
|
|
|
|
-
|
74 Mpa |
ASTM D790 |
|
-
|
58 Mpa |
ISO 178 |
|
弯曲模量
|
2080 Mpa |
ASTM D790 |
|
弯曲模量
|
1860 Mpa |
ISO 178 |
|
拉伸模量
|
1080 Mpa |
ISO 527 |
1 mm/min
|
摩擦系数
|
0.19 - |
ASTM D 3702 |
Dynamic COF
|
摩擦系数
|
0.24 - |
ASTM D 3702 |
Static COF
|
磨损因数
|
121 E-10 in5·min/ft·lb·hr |
ASTM D 3702 |
Wear Factor Washer
|
| 冲击性能 |
值/单位 |
测试标准 |
测试条件 |
悬臂梁缺口(Izod Notched)
|
|
|
|
23℃ (73℉)
|
106 J/m |
ASTM D256 |
|
23℃ (73℉)
|
11 kJ/m² |
ISO 180/1A |
80*10*4
|
悬臂梁无缺口(Izod Unnotched)
|
|
|
|
23℃ (73℉)
|
2034 J/m |
ASTM D4812 |
|
23℃ (73℉)
|
172 kJ/m² |
ISO 180/1U |
80*10*4
|
| 热学性能 |
值/单位 |
测试标准 |
测试条件 |
热变形温度(HDT)
|
|
|
|
0.45 Mpa (66 psi)（4.6kg/cm²）
|
140 °C |
ASTM D648 |
3.2 mm, unannealed
|
0.45 Mpa (66 psi)（4.6kg/cm²）
|
138 °C |
ISO 75/Bf |
Flatw 80*10*4 sp=64mm
|
1.8 Mpa (264 psi)（18.6kg/cm²）
|
121 °C |
ASTM D648 |
3.2 mm, unannealed
|
1.8 Mpa (264 psi)（18.6kg/cm²）
|
120 °C |
ISO 75/Af |
Flatw 80*10*4 sp=64mm
|
线性膨胀系数(CLTE)
|
|
|
|
纵向(Flow)
|
81.9 E-6/°C |
ASTM E831 |
-40°C to 40°C, flow
|
纵向(Flow)
|
82 E-6/°C |
ISO 11359-2 |
-40°C to 40°C, flow
|
横向(Across Flow)
|
88.9 E-6/°C |
ASTM E831 |
-40°C to 40°C, xflow
|
横向(Across Flow)
|
89 E-6/°C |
ISO 11359-2 |
-40°C to
|